M-996 Continuous Alumina Fiber
Description
M-996 is a continuous polycrystalline ceramic fiber grade for metal matrix composite reinforcement. Sol-gel precursor processing provides continuous filaments that can be woven, braided or incorporated into composite structures.
CHARACTERISTICS
- Continuous inorganic filaments
- Oxidation resistance
- High modulus and low thermal expansion
- Grade-specific oxide composition
SPECIFICATION
| Property | Specification |
|---|---|
| Grade | M-996 |
| Composition | ≥99% Al₂O₃ |
| Filament diameter | 9–12 µm |
| Nominal density | 3.8 g/cm³ |
| Spool length | 500–10000 m |
| Additional property | Reference value |
|---|---|
| Brochure melting point | 2050°C |
| Crystalline phases (Chinese brochure) | α-Al₂O₃ |
Melting point is distinct from the recommended operating temperature.
PERFORMANCE
| Property | Specification |
|---|---|
| Brochure long-term use temperature | 1000°C |
| Reported tensile property | 2.7 ± 0.3 GPa |
| Young’s modulus | 330 ± 30 GPa |
| Breaking elongation | 0.6 ± 0.3% |
Values are brochure reference data, not design allowables. Confirm specimen definition and test method before comparing yarn, bundle and single-filament results.
CUSTOMIZATION
Discuss yarn count, spool length, sizing, textile conversion and compatibility with the intended matrix.
APPLICATION
- Composite material development
- High-temperature textiles and thermal barriers
- Metal matrix composite reinforcement
CERTIFICATION
Specify the required technical data sheet, batch certificate of analysis and application test reports in your inquiry. Certification scope must be confirmed for the selected grade and manufacturing site; company management-system credentials do not replace product qualification.
Inquiry
Ask about: M-996 Continuous Alumina Fiber